Hot Rolled Steel Plates of 1.0038 S235jr Carbon Steel

Description: 1.0038 steel material properties according to EN 10025 standard, The numerical grade 1.0038 is the number for quality structural steel. It is an unalloyed steel and structural steel as defined in the EN 10025 standard. This steel is mainly used for formin...

If the standard size steel materials can not meet your demands, We aslo supply 1.0038 Steel processing service. you can find one-stop solution for various customized steel processing requirements: Large vessels, structural parts, semi-products, components, manufacturing supporting ...

Processing Service: Cutting, Welding, Drilling, Rolling, Bending, Forming, Grinding, Stamping and so on machining

E-mail: [email protected]

Whatsapp: +86-15690878691

Chat Online Leave a Message

1.0038 Steel Description

1.0038 steel material properties according to EN 10025 standard, The numerical grade 1.0038 is the number for quality structural steel. It is an unalloyed steel and structural steel as defined in the EN 10025 standard. This steel is mainly used for forming different forged products. 1.0038 is the numeral identification of the material grade S235JR.

We can provide 1.0038 carbon and low-alloy steel's precise chemical composition, mechanical properties in various states, heat treatment procedures for various purposes, as well as 100% ultrasonic testing, cold working, hot rolling, straightening, peeling, bending, welding or rough turning for the 1.0038 steel sheets.

1.0038 Carbon steel Type and Size:
Hot Rolled Width: 50MM~2200MM
Hot Rolled Thickness: 1.8MM~20MM
Cold Rolled Width: 500MM~1500MM
Cold Rolled Thickness: 0.2MM~3MM
Length: 4m,6m,8m or as requirement

1.0038 Carbon Steel and Mechanical Properties, Chemical Element, Cross Reference, Datasheet.

Heat treated : 1897°C - 1141°C

1.0038 Steel Datasheet

S235JR carbon steel plate specification	Thickness	≤400mm
	Width	≤4200mm
	Length	≤18000mm
Steel Number	1.0038
Standard	EN 10025
S235JR carbon steel plate density	7.85g/m3
Melting point	1420-1460 °C (2590-2660 °F)
Brinell hardness	below 120 HBW
Deep processing	Cutting, welding, bending, drilling, etc.
Third party inspection	SGS, BV, Intertek, etc.
Delivery state	HR, AR

1.0038 Steel Chemical composition

C	Si	Mn	P	S	Cr	Ni
0.20		1.40	0.035	0.035
Mo	Al	Cu	Nb	Ti	V	Ce
		0.55
N	Co	Pb	B	Other
0.012

1.0038 Steel Mechanical Properties

The minimum yield strength of 1.0038/S235JR steel shall be 235 Mpa for nominal thickness, and tensile strength of 1.0038 / S235JR steel shall be within 360-510Mpa. 1Mpa is equal to 1 N/mm2.

The 1.0038 steel material is referred to have low tensile strength on the other hand having a high ductility. The mechanical properties; low tensile and high ductility is relative to other wrought material grades available in the market.

Yield R_p0.2 (MPa)	Tensile R_m (MPa)	Impact KV/Ku (J)	Elongation A (%)	Reduction in cross section on fracture Z (%)	As-Heat-Treated Condition	Brinell hardness (HBW)
886 (≥)	317 (≥)	21	22	23	Solution and Aging, Annealing, Ausaging, Q+T,etc	343

The tensile strength of the 1.0038 non-alloy steel is expressed in Newton per millimeters and ranges from 340 to 520 N/mm2 (MPa) depending on the thickness as well.
The elongation property of 1.0038 steel varies with the heat treatment process and thickness but it is indicated typically 17 to 21%.
1.0038 can be welded by normal welding methods.
Carbon equivalence value is maximum 0.38 allowed.